Synthesis of High-solids Acrylic Resin with "Starved State" Technique

《南京理工大学学报》(自然科学版)[ISSN:1005-9830/CN:32-1397/N]

Issue:
2007年01期
Page:
129-133
Research Field:
Publishing date:
2007-02-28

Info

Title:
Synthesis of High-solids Acrylic Resin with "Starved State" Technique
Author(s):
SUN Zhi-juanZHANG Xin-yaHUANG HongCHEN Huan-qin
Institute of Chemical Engineering,South China University of Technology,Guangzhou 510641,China
Keywords:
acrylic resin high-solids / starved state0 polymerization technique property
PACS:
TQ320.7
DOI:
-
Abstract:
The acrylic resin with high solids is synthesized by the polymerization technique of / starved state0 feed. The factors that influence the properties of the resin are discussed, includimg monomers system, them ixture ratio of solvents, initiators and reactive temperature. The experimen- tal results show that using the feed technique of/ starved state0 can raise the conversion ratio ofmon- omers, shorten the reactive time and get polymersw ith much more even distribution of molecular weigh;t the technique of adding azobisisobutyronitrile (AIBN) as an initiator first and then benzo- peroxide( BPO) as another initiator at later stage of experiment can get higher initiating efficiency than using one initiator only. Furthermore, butyl acetate, dimethyl benzene and butanol are used as m ixture solvents because of low poison. W hen the m ixture ratio is 2B1B1, the system can keep good stability, the solid content ismore than 70% and the viscosity of polymers is appropriate. The pre- pared acrylic resin has outstanding properties, such as excellent adhesion, waterproo,f alkali and outdoorweather resistance. The acrylic resin can keep original shape after it is soaked for 96 hours in alkali solventw ith pH between 12 and 13, and the chrom atism value of quick ultraviolet less than 5% after seventy-hour ultraviolet irradiation.

References:

[ 1] 刘国杰, 耿耀宗. 涂料应用科学与工艺学 [M ]. 北京: 中国轻工业出版社, 1994.
[ 2] H am id J N, ShadpourM, Nader M. Synthesis and characterization of silicone-modified vinyl acetate– a- crylic emulsion copolymers [ J]. Progress in Organic Coatings, 2006, 55 ( 4): 375- 381.
[ 3] Diakumakos C D, JonesfN, Y eH, et a.l H igh solids marresistant clear coats prepared from an isophthalate- based oligoester and a melam ine resin [ J]. Journal of Applied Polymer Science, 2002, 83(6): 1 317- 1 327.
[ 4] 陆敏, 沈澄英. 丙烯酸钠与丙烯酸羟乙酯共聚高吸水性树脂研究 [ J]. 南京理工大学学报, 1999, 23 (6): 554- 559.
[ 5] G reenville L P. H igh-solids and powder coatings from hydroxy-functional acrylic resins [ P]. U S Patent: 5 646 213, 1997- 07- 08.
[ 6] Nakano S. Polycarbonate-modified acrylic polymers for coating materials [ J]. Progress in Organic Coatings, 1999, 35: 141- 151.
[ 7] BusiE, BasosiR. An innovative approach to the design of plastic antibodies: Molecular imprinting via a non- polar transition state analogue [ J]. Journal ofM olecu- lar CatalysisA: Chemica,l 2004, 217 (1): 31- 36.
[ 8] 吴进, 邱绕生, 王菊平. 高性能丙烯酸外墙涂料的研制 [ J]. 涂料工业, 1999( 9): 20- 22.
[ 9] Opera S, V lad S. Epoxy urethane acrylate [ J]. Euro- pean Polymer Journa,l 2000, 36 ( 2): 373- 378.
[ 10] 曹贵平, 乐慧慧, 张民华. /饥饿0反应器中苯乙烯聚合动力学 [ J]. 高校化学工程学报, 1995, 1( 9): 51- 57.
[ 11] Shim J S, W atts D C. Residualmonomer concentra- tions in denture-base acrylic resin after an additiona,l soft-liner, heat-cure cycle [ J]. Dental M aterials, 1999, 15 ( 4): 296- 300.
[ 12] 鲁建民, 刘亚康, 贺建芸. 用作粉末涂料的丙烯酸树脂合成工艺的正交优化 [ J]. 石油化工, 2001 ( 10): 760- 763.

Memo

Memo:
-
Last Update: 2007-02-28