炭黑的表面化学改性及其在水介质中的分散性研究
分享到：

《南京理工大学学报》（自然科学版）[ISSN:1005-9830/CN:32-1397/N]

卷:
期数:
2006年06期
页码:
778-782
栏目:
出版日期:
2006-12-30

文章信息/Info

Title:
Chemical Modification of Carbon Black Surface and Its Dispersibility in Water
作者:
赵军;徐复铭;周伟良;邹薇;
南京理工大学化工学院, 江苏南京210094
Author(s):
ZHAO Jun; XU Fu-ming; ZHOU Wei-liang; ZOU Wei
School of Chemical Engineering,NUST,Nanjing 210094,China
关键词:
炭黑;  表面;  化学改性;  分散稳定性
Keywords:
carbon black;  surface;  chem ica lmod ification;  d ispersible stab ility
分类号:
TQ127.13
摘要:
为了提高炭黑在水性介质中的分散性,利用对苯酚磺酸(p-PS)及低聚对苯酚磺酸(SPF)羟基邻位的活泼氢与羟甲基的反应,将炭黑羟甲基化后,研究了炭黑粒子表面导入亲水性基团的表面化学改性方法。研究了反应时间、反应溶剂对接枝率的影响,并在水浴90℃,催化剂存在下,水/甲醇为溶剂,反应3h,得到了接枝率为13%的改性炭黑。通过FTIR、TEM等手段对p-PS和SPF改性炭黑进行了表征;未经改性的炭黑5m in即会完全沉降;p-PS改性炭黑,在自然沉降15 d后,分散液透光率从1.5%增加到11.4%;接枝率为13%的SPF改性炭黑,分散液透光率从43.4%变为65.8%。结果表明:改性炭黑在水中的分散稳定性大大提高。
Abstract:
By means of the h igh react iv ity betw een hydroxym ethy l groups and the active hydrogen o f p-phenol su lfonic ac id ( p-PS) and the o ligomer o f p-PS and fo rma ldehyde ( SPF), hydroxymethy-l ized carbon black w as further reacted w ith p-PS and SPF. The effects o f the react ion time and the solvent on the gra ft ing y ield are investigated, and amodified carbon black w ith 13% grafting y ie ld is obta ined after reacting 3 hours in methano l and w ater so lvent w ith ca tslyst at 90e . The grafted and ungrafted carbon black are characterized by FTIR spectrum and TEM. D eposition experiments show that the unmod ified carbon b lack in suspension sed imentates in 5m in. The ultrav io le t transm ittance of p-PS carbon b lack /w ater suspension increases from 1. 5% to 11. 4% and that o f carbon b lack grafted w ith 13% SPF increases from 43. 4% to 64. 8% after 15 days. deposition. The resu lts show that the d ispersible stab ility of the mod ified carbon in w ater is greatly improved.

参考文献/References:

[ 1] ShinozukaM, NakamuraH, KanbayashiK, et a.l Ink for use in ink je t reco rd ing [ P ]. JP: WO9107470, 1991.
[ 2] T subkawa N, H osoyaM, Kum ada J. G ra fting rea tion o f surface ca rboxy l g roups on carbon b lack w ith po lym ers hav ing term ina l hydroxy l o r am ino groups us ing N, N. -d icyc lohexy lcarbod iim ide as a condens ing agent [ J]. Reactive and Functiona l Polym ers, 1995, 27 ( 1): 75- 81.
[ 3] Pa rk S J, K im J S. Influence of plasm a treatm ent on m ic rostructures and acid-base surface energetics of nanostructured carbon b lack: N2 plasm a env ironm ent [ J] . J Co llo id Interface Sc,i 2001, 244 ( 2): 336 - 341.
[ 4] Pa rk S J, Cho K S, Ryu S K. F iller-e lastm er in teraction: Influence o f oxygen plasma trea tm en t on surface and m echanica l prope rties of carbon black / rubber composites [ J ]. Cabon, 2003, 41 ( 7 ) : 1 437 - 1 442.
[ 5] 陈尔洽. 色素炭黑的氧化处理[ J]. 涂料工业, 1998 ( 4): 18- 19.
[ 6 ] 李志强, 赵焱, 陈敏. 色素炭黑表面聚丙烯酸接枝 改性制备染料[ J]. 四川大学学报, 2003, 40 ( 1 ): 122- 126.
[ 7 ] 李玮, 谢志明, 李卓美. 聚丙烯酸酯接枝炭黑的合 成、表征及其应用[ J] . 功能高分子学报, 1999, 12 ( 3): 302- 306.
[ 8 ] 李玮, 谢志明, 李卓美. 丙烯酸酯接枝炭黑无皂水 性涂料的性能研究[ J]. 功能高分子学报, 2002, 15 ( 2): 181- 184.
[ 9] 季军晖. 炭黑表面接枝及其分散性的研究[ D] . 天 津: 天津大学化工学院, 1997.

相似文献/References:

[1]关富玲,张惠峰.桁架式可展开天线反射面精度试验[J].南京理工大学学报(自然科学版),2009,(03):325.
　GUAN Fu-ling,ZHANG Hui-feng.Reflector Surface Precision Experiment of Deployable Truss Antenna[J].Journal of Nanjing University of Science and Technology,2009,(06):325.
[2]沈守范.滚珠丝杠付返珠器正螺旋面型回珠曲线的计算[J].南京理工大学学报(自然科学版),1979,(01):103.

备注/Memo

备注/Memo:
作者简介: 赵军( 1973- ), 男, 辽宁义县人, 博士生, 主要研究方向: 材料学, E-mail:slamjun@ yahoo. com. cn; 通讯 作者: 徐复铭( 1946- ) , 男, 教授, 博士生导师, 主要研究方向: 含能材料, E-mail: wlzhou@ mail.njust.edu. cn。
更新日期/Last Update: 2006-12-30