HTPB/HMX复合粒子的制备及其机械感度研究
分享到：

《南京理工大学学报》（自然科学版）[ISSN:1005-9830/CN:32-1397/N]

卷:
期数:
2009年02期
页码:
267-271
栏目:
出版日期:
2009-04-30

文章信息/Info

Title:
Preparation and Mechanical Sensitivity of HMX/HTPB Composite Particles
作者:
安崇伟1;  2;  郭效德1;  谢五喜3;  宋小兰1;  王 毅1;  李凤生1
1. 南京理工大学化工学院, 江苏南京210094; 2. 中北大学化工与环境学院, 山西太原030051; 3. 西安近代化学研究所推进剂研究部, 陕西西安710065
Author(s):
AN Chong-wei1; 2; GUO Xiao-de1; XIE Wu-xi3; SONG Xiao-lan1; WANG Yi1; LI Feng-sheng1
1.School of Chemical Engineering,NUST,Nanjing 210094,China;2.Chemical Industry and Ecology Institute,North University of China,Taiyuan 030051,China;3.Department of Propellants,Xi’an Modern Chemistry Research Institute,Xi’an 710065,China
关键词:
奥克托今;  端羟基聚丁二烯;  表面包覆;  复合粒子;  机械感度
Keywords:
cyclotetramethylene tetranitramine;  hydroxyl terminated polybutadiene;  surface coating;  composite particles;  mechanical sensitivity
分类号:
TQ564
摘要:
为了降低奥克托今(HMX)的机械感度,以端羟基聚丁二烯(HTPB)和甲苯二异氰酸酯(TDI)为包覆材料,采用相分离法对HMX颗粒进行了表面包覆,制备了HTPB/HMX复合粒子。采用SEM和XPS对包覆样品进行表征,对包覆前后样品的机械感度进行测试和对比。探讨了包覆工艺对包覆效果和机械感度的影响,并分析了包覆机理和钝感机理。结果表明,当用HT-PB和TDI同时包覆时,样品易出现大块粘连,摩擦感度降低,而撞击感度不降反升。经1%(质量分数)HTPB包覆后,HMX的摩擦爆炸概率P由100%降至46%,特性落高H
Abstract:
To reduce the mechanical sensitivity of cyclotetramethylene tetranitramine(HMX),hydroxyl terminated polybutadiene(HTPB) and toluene diisocyanate(TDI) are used to coat HMX by the method of phase separation.The coated samples are characterized by SEM(scanning electron microscope) and XPS(X-ray photoelectron spectrometry).The mechanical sensitivity of unprocessed and coated HMX samples are measured and contrasted.The influence of coating processing on coating effect and mechanical sensitivity are discussed,and the coating mechanism and insensitive mechanism are analyzed.The results show that when coated with HTPB and TDI simultaneously,the samples form agglomeration easily and their friction sensitivity reduces,however the impact sensitivity increases.After coated with 1% HTPB,the drop height H50 of HMX decreases from 32.5 cm to 28.6 cm and explosion probability P decreases from 100% to 46%.When firstly coated with HTPB and then with TDI,the samples disperse well and the coating layers become even.The mechanical sensitivity reduces obviously.When the covering mass amount of HTPB is 1%,H50 increases to 45.7 cm,and P decreases to 32%.

参考文献/References:

[ 1] 5炸药理论6编写组. 炸药理论[M ]. 北京: 国防工业出版社, 1982. 29- 30.
[ 2] 黄明, 李洪珍, 徐容, 等. 降感黑索今研究[ J]. 含能材料, 2006, 14( 6): 492.
[ 3] 刘玉存, 王建华, 安崇伟, 等. RDX 粒度对机械感度的影响[ J]. 火炸药学报, 2004, 27( 2): 7- 9.
[ 4] 李文. 黑索今和奥克托今的化学钝感及相关问题研究[ D ]. 北京: 北京理工大学化工与环境学院, 1995. 10- 11.
[ 5] 安崇伟, 宋小兰, 王毅, 等. 硝胺类炸药颗粒表面包覆的研究进展[ J]. 含能材料, 2007, 15( 2): 188- 192.
[ 6 ] Mann ing. Reduction of ene rgetic filler sensitivity in prope llants through coating[ P]. USP 6524706, 2003.
[ 7] 王晓丽, 焦清介, 李国新, 等. 钝化黑索今薄膜及其感度的研究[ J]. 火工品, 2003( 3): 23- 26.
[ 8] 张树海, 苟瑞君, 张景林, 等. 硝胺炸药的超临界溶液快速膨胀包覆技术研究[ J] . 火工品, 2004( 2): 20- 26.
[ 9] Smi pson R L, Urtiew P A, Ornellas D L, et a.l CL-20 perform ance ex ceeds that of HMX and its sensitiv ity is moderate[ J]. Prop Expos Py rotech, 1997, 22: 249- 255.
[ 10] 陆铭, 陈煜, 罗运军, 等. 水性聚氨酯乳液的制备及其包覆RDX 的研究[ J]. 推进技术, 2005, 26 ( 1): 89- 92.
[ 11] Som oza. Process for reduc ing sensitiv ity in explosives [ P]. USP 5279492, 1994.
[ 12] 潘碧峰, 张磊, 罗运军, 等. 树形键合剂包覆RDX及其相互作用研究[ J]. 推进技术, 2003, 24( 5): 470 - 473.
[ 13] GJB /772A- 1997. 中华人民共和国国家军用标准. 感度和安全性试验方法[ S].

备注/Memo

备注/Memo:
基金项目: 国家自然科学基金( 50602024, 50306008)
作者简介: 安崇伟( 1980 - ) 男, 博士生, 主要研究方向: 含能材料的细化、表面包覆及其在推进剂中的应用, E-ma il:acw 98081b1@ 163. com; 通讯作者: 李凤生( 1946- ), 男, 教授, 博士生导师, 主要研究方向: 超细粉体技术、固体火箭推进剂设计与制造。
更新日期/Last Update: 2012-11-19