多层金属板爆炸焊接研究
分享到:

《南京理工大学学报》(自然科学版)[ISSN:1005-9830/CN:32-1397/N]

卷:
期数:
2009年05期
页码:
596-599
栏目:
出版日期:
2009-10-30

文章信息/Info

Title:
Explosive Welding of Multilayer Metal Plates
作者:
孙宇新 1 2 康宗维 1 付艳恕 1 李 强 1 2 王晓萍 1
1.南京理工大学瞬态物理国家重点实验室,江苏南京210094; 2. 中国电子科技集团公司第27所, 河南郑州450000
Author(s):
SUN Yu-xin12KANG Zong-wei1FU Yan-shu1LI Qiang12WANG Xiao-ping1
1.National Key Laboratory of Transient Physics,NUST,Nanjing 210094,China;2.The 27th Research Institute,China Electronics Technology Group Corporation,Zhengzhou 210094,China
关键词:
多层金属板 爆炸焊接 撞击速度 焊接下限 硬度
Keywords:
multilayer metal plates explosive welding impact velocity inferior limit hardness
分类号:
TG456.6
摘要:
为了获得焊接后性能稳定的多层金属板,该文通过调节金属板层间间距和添加撞击板,对七层和十一层铝板进行了爆炸焊接研究。将层合材料进行切割分析,由结合界面的显微金相照片可知块体焊接质量良好;显微硬度分析表明,材料结合界面附近区域硬度有所增加且各界面处硬度波动不大,证明各层的相互撞击速度基本一致。该文研究结果为控制层间撞击速度,使其达到基本一致,且接近焊接下限提供了解决方法。
Abstract:
In order to obtain the multilayer metal plates with stable property after welding,the spaces between two metal plates are regulated,an impact plate is added,and the explosive welding experiment on the seven-layer and eleven-layer aluminum plates are done.The multilayer plates are cut and analyzed.The metallographs of the bonding interfaces show that the bonding wave is small and good.The micro-hardness analysis indicates that the hardness near the interface is higher and each welding interface is approximate,concluding that the impact velocity of each layer is similar.The results provide a solution to the problems of how to control the impact velocity and how to make the impact velocity for each layer approximately equal and close to the inferior limit in the explosive welding of multilayer metal plates.

参考文献/References:

[ 1] 张建臣, 杨文彬,孙明, 等. 多层爆炸焊接参数的试验研究[ J]. 焊接技术, 2002, 31(3): 15-17.
[ 2] Hokamoto K, ChibaA, FujitaM. Single-shot explo-sivewelding technique for the fabrication of multilay-eredmetal base composites: effect ofwelding parame-ter leading tooptimumbonding condition[ J]. Compos-tionEngineering, 1995, 5( 8): 1069-1079.
[ 3] 王飞, 王伟策, 王耀华, 等. 多层A-lTi复合板爆炸焊接实验研究[ J]. 工程爆破, 2002, 8( 4): 7-10.
[ 4] 邵丙璜, 张凯. 爆炸焊接原理及其工程应用[M]. 大连: 大连工学院出版社1987. 190-197.
[ 5] 李晓杰, 杨文彬, 奚进一, 等. 双金属爆炸焊接下限[ J]. 爆破器材, 1999, 28(3): 22-26.
[ 6] 郑远谋, 黄荣光, 陈世红. 爆炸复合材料中金属的硬化[ J]. 矿冶, 1999, 8( 3): 60- 64.
[ 7] 郑远谋, 黄荣光, 陈世红. 爆炸复合材料中金属的强化[ J]. 工程爆破, 2000, 6( 1): 25- 31.

备注/Memo

备注/Memo:
基金项目: 国防基础科研项目; 高等学校博士学科点专项科研基金( 20070288070); /十一五0兵器预研支撑基金
作者简介: 孙宇新( 1970- ), 男, 博士, 副教授, 主要研究方向: 穿甲、爆炸效应及其应用, E-mail:yxsun@mail.njust. edu. cn。
更新日期/Last Update: 2012-11-19