聚碳酸酯高应变率分离式霍普金森压杆实验研究
分享到:

《南京理工大学学报》(自然科学版)[ISSN:1005-9830/CN:32-1397/N]

卷:
36卷
期数:
2012年03期
页码:
529-533
栏目:
出版日期:
2012-06-30

文章信息/Info

Title:
Experimental Investigation of Polycarbonate at High Strain Rate by SHPB
作者:
孙朝翔; 鞠玉涛; 胡少青; 郑亚;
南京理工大学机械工程学院;
Author(s):
SUN Chao-xiangJU Yu-taoHU Shao-qingZHENG Ya
School of Mechanical Engineering,NUST,Nanjing 210094,China
关键词:
聚碳酸酯 高应变率 分离式霍普金森压杆 二波法 屈服强度 温度软化
Keywords:
polycarbonate high strain rates split Hopkinson pressure bar two-wave methods yield strength temperature-softening
分类号:
O347.3
摘要:
为获得聚碳酸酯(PC)在环境温度范围内的动态力学特性,该文利用分离式霍普金森压杆技术对PC进行高应变率动态压缩力学实验。在低温-50℃、常温+15℃和高温+50℃三种温度下进行实验,并对实验数据有效性进行检验。用二波法对数据进行处理,得到PC在不同应变率下的应力应变曲线。基于应力应变曲线分析了应变率和温度对PC动态压缩特性的影响。实验结果表明PC具有明显的应变率相关性。在高应变率下,PC的屈服强度约为静态下的1.6倍。在动态下,屈服应力随着应变率的增加不断增加,与应变率常用对数呈线性增长关系。PC也具有对温度的敏感性,其屈服应力随着温度的升高而降低,表现为温度软化效应。在-50~+50℃范围内,PC力学特性基本一致,屈服应力变化幅值不超过6%。
Abstract:
In order to obtain the dynamic mechanical properties of polycarbonate(PC)material in ambient temperatures,high strain rate dynamic compressive mechanics experiments of PC are done using split Hopkinson pressure bar(SHPB)technique at three different ambient temperatures:-50 ℃、+15 ℃ and +50 ℃.The availability of the data is examined.The data are dealt with one-wave method,and the stress-strain curves of PC in different strain rates are obtained.The effects of strain rates and temperatures on dynamic compression behaviors of PC are analyzed based on the stress-strain curves.The result suggests that PC is a significant strain rate dependent material.The yield strength of PC increases at high strain rates,which is approximately 1.6 times higher than that under quasi-static.The yield stress increases with the strain rate,showing a linear growth relationship with the logarithm of the strain rate.PC is sensitive to temperature.The yield stress decreases with the increase of temperature showing temperature softening effect.When temperature ranges in-50~+50 ℃,the mechanic performances of PC almost remain the same,and the change range of the yield stress is not more than 6%.

参考文献/References:

[1] Christmann A, Ienny P,Quantin J C, et al. Mechanical behaviour at large strain of polycarbonate nanocomposites during uniaxial tensile test[J]. Polymer, 2011, 52( 18) : 4033-4044.
[2] Perez J M,Vilas J L,Laza J M,et al. Effect of reprocessing and accelerated ageing on thermal and mechanical polycarbonate properties[J]. Journal of Materials Processing Technology, 2010, 210( 5) : 727-733.
[3] Arnold J C,Taylor J E. Improved thermodynamic approach for predicting the ESC behavior of polycarbonate in binary liquid mixtures[J]. Journal of Applied Polymer Science, 1999, 71( 13) : 2155-2161.
[4] Kayano Y,Keskkula H,Paul D R. Fracture behaviour of polycarbonate blends with a core-shell impact modifier[J]. Polymer, 1998, 39( 4) : 821-834.
[5] Sarva S,Mulliken A D,Boyce M C. Mechanics of taylor impact testing of polycarbonate[J]. International Journal of Solids and Structures, 2007, 44( 7/8) : 2381-2400.
[6] 胡文军,张方举,田常津,等. 聚碳酸酯的动态应力应变响应和屈服行为[J]. 材料研究学报,2007,21 ( 4) : 439-443.
Hu Wenjun,Zhang Fangju,Tian Changjin,et al. Dynamic stress-strain response and yield behavior of polycarbonate[J]. Chinese Journal of Materials Research, 2007, 21( 4) : 439-443.
[7] 胡文军,唐录成,张方举,等. 聚碳酸酯冲击压缩的实验研究[J]. 高分子材料科学与工程,2006,22 ( 6) : 165-168.
Hu Wenjun,Tang Lucheng,Zhang Fangju, et al. Experimental study of polycarbonate’s impact compression[J]. Polymer Materials Science and Engineering, 2006, 22( 6) : 165-168.
[8] Kolsky H. An investigation of the mechanical properties of materials at very high rates of loading[J]. Proceedings of the Physical Society. Section B, 1949, 62( 11) : 676-700.
[9] Gama B A,Lopatnikov S L,Gillespie J W. Hopkinson bar experimental technique: A critical review[J]. Applied Mechanics Reviews, 2004, 57( 1/6) : 223-250.
[10] 胡功笠,刘荣忠,齐爱东,等. 混凝土材料的SHPB 试验及动态性能分析[J]. 南京理工大学学报, 2005, 29( 4) : 420-424.
Hu Gongli,Liu Rongzhong,Qi Aidong. et al. SHPB experiment and dynamic properties of concrete [J]. Journal of Nanjing University of Science and Technology, 2005, 29( 4) : 420-424.
[11] 王晓燕,卢芳云,林玉亮. SHPB 实验中端面摩擦效应研究[J]. 爆炸与冲击, 2006, 26( 2) : 134-139.
Wang Xiaoyan,Lu Fangyun,Lin Yuliang. Study on interfacial friction effect in the SHPB tests[J]. Explosion and Shock Waves, 2006, 26( 2) : 134-139.
[12] 宋力,胡时胜. SHPB 数据处理中的二波法与三波法[J]. 爆炸与冲击, 2005, 25( 4) : 368-373.
Song Li,Hu Shisheng. Two-wave and three-wave method in SHPB data processing[J]. Explosion and Shock Waves, 2005, 25( 4) : 368-373.
[13] 宋力,胡时胜. SHPB 测试中的均匀性问题及恒应变率[J]. 爆炸与冲击, 2005, 25( 3) : 207-216.
Song Li,Hu Shisheng. Stress uniformity and constant strain rate in SHPB test[J]. Explosion and Shock Waves, 2005, 25( 3) : 207-216.

更新日期/Last Update: 2012-10-12